Abstract
ABSTRACTThe modification of the wear properties of type Ha diamond following ion implantation with 100 keV carbon and nitrogen has been studied at implantation temperatures of 150 and 470 K. Abrasion testing using low load multiple pass scratch testing with a Rockwell diamond indenter has shown a decrease in wear resistance. Microstructural modifications resulting from ion implantation have been assessed using Channeling Rutherford Backscattering Spectroscopy (C-RBS). No correlation was found between the presence of ion beam induced point defects (as measured by C-RBS) and the increase in wear. There are no obvious wear rate differences observed for nitrogen or carbon implantation.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.