Abstract
AbstractGraphene prepared by the thermal reduction of graphite oxide was modified by reactions with methanol or 1‐butanol using aqueous HBF4 solution as a catalyst. Results showed that the reaction created hydroxyl groups on the graphene and at the same time reduced the number of defects. Gravimetry, thermogravimetry, X‐ray photoelectron spectroscopy and Fourier transform infrared spectroscopy showed that the alcohols had reacted with epoxide groups on graphene. Raman spectroscopy showed that the defects in the graphene were repaired through other accompanying reactions. The reinforcing effect of graphene, observed in the tensile properties and the shape memory behavior of graphene/polyurethane composites, was increased when the graphene was modified with methanol. However, decreases in density and glass transition temperature were evident for the composites made with alcohol‐modified graphene. These results show that the newly created hydroxyl groups on graphene produce effective covalent bonds with the polyurethane chains of the matrix; however, the increased number of bonds restricts the rearrangement of the matrix molecules for dense packing. The covalent bonds between graphene and polyurethane chains enhanced shape recoverability and reduced the hysteresis brought about by repeated thermomechanical cycles. Copyright © 2012 Society of Chemical Industry
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.