Abstract
In this study, pure mode I, pure mode II and mixed mode fracture behavior of an epoxy were investigated. Specifically, the mixed mode values of fracture toughness and critical strain energy release rate (CSERR) were measured. Specimens were subjected to mixed mode loading using compact tension shear (CTS) test. Some experimental modifications were found to be necessary to eliminate rotation and ensure crack propagation at the notch when testing epoxy specimens at high mode II loading. A failure criterion for the mixed mode loading of polymer is developed and its predictions are compared with the experimental results. The crack propagation direction in epoxy was investigated in this research as well. A detailed study of failure mechanisms on the fracture surface was performed. The results indicate that the increase in the value of toughness can be directly related to the fracture morphology.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.