Abstract
The improvement of mechanical properties and the microstructure evolution through adding Sc to AZ61magnesium alloy were studied. The results indicated that the Mg17Al12 phase in the extruded AZ61 alloy was mainly distributed around the sub-structured and fine deformed grains, resulting in the nonuniform microstructure. The addition of Sc could effectively suppress the band-like precipitation of Mg17Al12 phase and improve the uniformity of microstructure. The grain sizes of the extruded alloys showed a trend of first decreasing and then increasing with the increase of Sc, which was mainly attributed to the secondary phase. The AZ61–0.5Sc alloy exhibited the best mechanical properties, its ultimate tensile strength and yield strength were 14.8MPa and 40.8MPa higher than those of the extruded AZ61 alloy, respectively, which was ascribed to the fine grains and abundant secondary phase in the alloy.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call