Abstract
The effect of Ti-rich (Ti,V)(C,N) precipitates on the evolution of intragranular ferrite in the coarse grain heated effected zone (CGHAZ) of V–N–Ti steel was systematically investigated via transmission electron microscopy. The coarse grain boundary ferrite, bainite, and ferritic side-plates in simulated CGHAZ were replaced by polygonal ferrite and acicular ferrite, when the nitrogen content was increased from 0.0044wt% to 0.0094wt%. In addition, the undissolved Ti-rich core acted as a nucleation site for the V-rich cap; the cap reached the critical size at which nucleation of intragranular ferrite occurs nucleation size of intragranular ferrite with the aid of the core. Owing to a cap-induced increase in the nucleation potency, the intragranular ferrite have formed on the Ti-rich (Ti,V)(C,N) hold the Baker-Nutting orientation relationship ((001)IGF//(001)(Ti,V)(C,N), [110]IGF//[100](Ti,V)(C,N)).
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.