Abstract
The cleavage resistance of two microalloyed steels (steels A and B) was studied using several tests, including the instrumented precracked Charpy and Charpy V-notch (CVN) techniques. Ductile-to-brittle transition temperatures were measured for the base-metal and simulated heat-affected zone (HAZ) microstructures. Steel B showed inferior cleavage resistance to steel A, and this could not be explained by differences in gross microstructure. Scanning electron fractography revealed that TiN inclusions were responsible for cleavage initiation in steel B. These inclusions were well bonded to the ferritic matrix. It is believed that a strong inclusion-matrix bond is a key factor in why TiN inclusions are potent cleavage initiators in steel. Strong bonding allows high stresses in a crack/notch-tip plastic zone to act on the inclusions without debonding the interface. Once an inclusion cleaves, the strong bond allows for transfer of the TiN crack into the ferritic matrix. It was estimated that only 0.0016 wt pct Ti was tied up in the offending inclusions in steel B. This indicates that extended times at high temperatures during the casting of such steels could produce TiN-related toughness deterioration at even modest Ti contents.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.