Abstract
Black iron–chromium (Fe–Cr) bearing oxide pigments are generally utilised as effective colourants in a wide variety of applications. However, in the case of their use within ZnO-containing glazes, they yield an undesirable brown colour instead of expected black colour. In order to understand the colour change in this system, we report the use of focused ion beam (FIB) sample preparation technique followed by the use of analytical transmission electron microscopy (TEM) characterisation techniques. According to the results, the formation of a reaction layer between the pigment and glaze was identified with an average composition of Zn 0.48Fe 0.79Cr 1.32O 4. Additionally, the valance of Fe was determined as 3+ in the pigment grain, whereas 2+ in the reaction layer and the glaze, respectively. Therefore, it was concluded that the colour change is occurring as result of the valence variation of Fe, the formation of Zn 0.48Fe 0.79Cr 1.32O 4 compound and the outward diffusion of Fe into the glaze.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.