Abstract
Multifunctional optical nanomultilayers (NMs) are needed for a wide array of applications, ranging from optical windows to electronic screens. Since the individual material constituents in optical coatings are often selected only for their desirable optical properties, mechanical characterization of the optical nanomultilayers is typically limited. Here, AlN/SiO2, TiO2/SiO2, and AlN/Al2O3 nanomultilayers synthesized in non-optimized and optimized optical performance layer configurations are tested using microtensile, nanoindentation, and pillar splitting techniques to highlight the effects of optical optimization on mechanical performance. Trends within each type of test and across all deformation modes reveal that layer thickness, volume fraction, and interfacial crystallinity can be viewed as controlling features for optical and mechanical performance, although their correlation may vary. It was observed that both configurations of the AlN/Al2O3 NMs exhibit the highest mechanical performance across all three testing techniques with an average experimental transmittance of 93.8% for the optimized layer configuration. Overall, the results from this expanded view of mechanical properties in ceramic optical nanomultilayers suggest the possibility of tuning film characteristics for joint optimization of opto-mechanical nanomultilayered coatings.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.