Abstract
Thermoplastic natural rubber hybrid composites reinforced with kenaf and short glass fibers were compounded by melt blending method using an internal mixer, Thermo Haake 600P. Thermoplastic natural rubbers (TPNR) were prepared from polypropylene (PP), natural rubber (NR) and liquid natural rubber (TPNR) with ratio 70:20:10, which were blended using internal mixer for 12 minutes at 180°C and rotor speed 40 r.p.m. Glass fiber was treated with silane coupling agent while TPNR reinforced kenaf fiber composite is using MAPP as a compatibilizer. TPNR hybrid composite with kenaf/glass fibers was prepared with fiber content (5, 10, 15, 20 volume % of fiber). Mechanical properties of the composites were investigated using tensile test[ 1 ], flexural, impact, and hardness test and scanning electron microscope (SEM)[ 1 ]. The incorporation of the treated or untreated fiber into TPNR has result in an increment of almost 100% of flexural modulus and impact strength as compared to TPNR matrix. However, the maximum strain decreased with increasing fiber content. The optimum composition for hybrid composite is at the fiber ratio of 30% kenaf fiber and 70% glass fiber. The SEM micrograph had shown, that the composite with coupling agent or compatibilizer promote better fiber-matrix interaction.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.