Abstract
Large negative magnetoresistance (MR) is observed in Fe–xCr–10Co (x=10,20,30,40,50,- 60,70, and 80 wt %) ternary heterogeneous alloy films prepared by the IBS (ion beam sputter) deposition process. All the as-deposited films consisted of the α phase alone. After aging treatment, the α phase is decomposited into two phases: the α1 (Fe–Co rich phase) and α2 (Cr rich phase). In the granular alloy, the GMR effect is obtained by virtue of the interface scattering between α1 and α2. After isothermal aging at 400 °C for 1 h, the largest MR of −27% appears around the Cr content of 60 wt % at 77 K and 14 kOe. The MR ratio of Fe–50Cr–10Co and Fe–70Cr–10Co is −12% and −20%, respectively, at the same condition. The MR ratio is also obviously effected by the Cr (or Fe) content in the alloy system.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.