Abstract
The amorphous FeCuNbSiB ribbons were first annealed at the temperature of 450 oC and 540 oC, respectively. Then, these annealed ribbons were milled into flake particles with the same condition. The different annealing temperature made the ribbons have the different crystallinities, which caused the milled particles have the different structures, morphologies, and magnetic properties. As for the flake particles by milling the ribbons annealed at 540 oC, they had higher crystallinity, smaller size, lower coercivity, and higher complex permeability compared with those by milling the annealed ribbons at 450 oC.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.