Abstract
In the present work, the localized corrosion and stress corrosion cracking (SCC) behaviors of a commercial 6005A-T6 aluminum extrusion profile was studied comprehensively. The velocity of crack growth in self-stressed double-cantilever beam (DCB) specimens under constant displacement was estimated, which also provides insight into the local microstructure evolutions at the crack tips caused by the localized pitting corrosion, intergranular corrosion (IGC), and intergranular SCC. Characterizations of local corrosion along the cracking path for a period of exposure to 3.5% NaCl were revealed via optical microscope (OM), scanning electron microscope (SEM), and electron backscatter diffraction (EBSD). The typical features of the pits dominated by the distribution of precipitates included the peripheral dissolution of the Al matrix, channeling corrosion, intergranular attack, and large pits in the grains. The discontinuous cracking at the crack tips indicated the hydrogen-embrittlement-mediated mechanism. Moreover, the local regions enriched with Mg2Si and Mg5Si6 phases and with low-angle grain boundaries presented better SCC resistance than those of the matrix with high-angle grain boundaries, supporting a strategy to develop advanced Al–Mg–Si alloys via interfacial engineering.
Highlights
With the quick development of the high-speed railway and the operation of the China Railway High-speed service for more than a decade, one of the greatest challenges is the management/maintenance of these trains in environmental conditions [1,2,3]
Based on our previous investigations of the local corrosion features of the 6005A-T6 alloy [2], we found that the Mg/Si ratio is a critical indicator in the development of novel, advanced, corrosion-resistant Al alloys, since the Si–Al interface and primary α-Al matrix remained unattached, presenting much better intergranular corrosion (IGC) resistance than that of the 5083-H111 and 6082-T6 alloys
We found that those main cracking paths are almost all along the precipitationfree zones (PFZs), while the pits occur with a lot of discontinuous precipitates nearby
Summary
With the quick development of the high-speed railway and the operation of the China Railway High-speed service for more than a decade, one of the greatest challenges is the management/maintenance of these trains in environmental conditions [1,2,3]. In order to support the foundations for interactive corrosion risk management, it is essential to reveal the foundations of environmentally induced cracking caused by corrosion [4,5]. Through increasing the concentration of Cu in Al–Mg–Si alloys, their strength can be improved [9], and the decomposition sequence can be changed by enhancing the number of possible phases and the complexity of the precipitation sequence [9,10,11]. The size and the morphology of precipitates play important roles in improving both the strength and the corrosion resistance of Al alloys [9,12,13,14,15]. The contributions of precipitation, high-angle grain boundaries (HAGBs), low-angle grain boundaries (LAGBs), and the hydrogen-assisted cracking were experimentally and theoretically evaluated, paving a path to the development of advanced, SCC-resistant Al–Mg–Si alloys
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.