Abstract
AbstractThickness dependence of ferroelectric and structural properties of BaTiO3 thin films were investigated. Stoichiometric BaTiO3 thin films were prepared by off-axis rf magnetron sputtering on polycrystalline Pt substrates at 700°C. Film thickness range was 2,100–20,000Å. Room temperature permittivity, frequency dependence of permittivity, and D-E hysteresis loops were measured and lattice parameters were determined as a function of the film thickness. It has been found that these properties had the strong dependence on film thickness, which was mainly due to grain sizes of BaTiO3 thin films. The main cause of thickness dependence of dielectric properties was thought to be crystallinity and stresses of thin films which is resulted from changes in grain sizes.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.