Abstract
A series of compounds with the general formula RE1.90Y0.10Zr2O7 (where RE includes Eu, Sm and Y includes La, Sm, Eu) were synthesized using a solid-state reaction method. These compounds were analyzed through differential thermal analysis (DTA), thermogravimetric analysis (TG), X-ray powder diffraction (XRD), and scanning electron microscopy (SEM). Additionally, their dielectric constant, loss tangent, piezoelectric charge constant, and Curie temperature were measured using an LCR meter, d33 meter, and TG/DTA. X-ray diffraction results indicated that all samples crystallize in a cubic pyrochlore structure. Photoluminescence studies revealed that Eu3+ ions predominantly contribute to the emission, whether as activators or co-activators. Among the phosphors, Eu1.90La0.10Zr2O7 exhibited a significantly longer afterglow compared to Sm1.90Eu0.10Zr2O7 and Eu1.90Sm0.10Zr2O7. Conversely, Sm1.90Eu0.10Zr2O7 demonstrated luminescence intensity that was 20 times greater than that of Eu1.90La0.10Zr2O7 and Eu1.90Sm0.10Zr2O7. Furthermore, all samples with characteristic Eu3+ emissions also exhibited piezoelectric properties. Curie temperature (Tc) of Eu1.90La0.10Zr2O7, Sm1.90Eu0.10Zr2O7, and Eu1.90Sm0.10Zr2O7 are 770°C, 830°C, and 845°C, respectively. Therefore, Sm3+ ion improves piezoelectric properties and Curie temperature when doping into the Eu2Zr2O7 host crystal.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Luminescence : the journal of biological and chemical luminescence
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.