This work aims to identify a suitable material for use as a zinc electrode substrate material in alkaline media, then employ this to study the effect of electrolyte flow rate and current density on zinc-nickel flow cell performance. Three metallic and four graphite composite materials are investigated, with the coulombic efficiency of zinc electrode charge / discharge cycling found to increase as hydrogen evolution onset potentials become more negative. A graphite / PVDF composite substrate demonstrates the highest coulombic efficiency at 96.7% and the most negative hydrogen evolution onset potential at -1.595 V vs. Hg/HgO. Using this material, the effect of electrolyte flow rate and current density on a zinc-nickel flow cell is investigated. Zinc morphology and flow cell performance is related to the ratio of applied current density to limiting current density. At values between 0.47 and 1, boulder type zinc morphologies occur, with smooth and compact zinc deposits resulting from current density ratios of 0.39 and below. Stable zinc-nickel flow cell performance is achieved over 200 cycles with coulombic, voltaic and energy efficiencies of 98.3, 88.1 and 86.6%, respectively, at a current density of 20 mA cm−2.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.