Abstract
ABSTRACTIn this work, the effect of hard tribological coatings was studied in terms of mitigating impact damage between tungsten carbide spherical elements and two different types of steel substrates. The coatings included a hard, highly elastic Tungsten-incorporated diamond-like carbon (W-DLC) coating at two different thicknesses and a harder, less elastic CrxN coating. Impacts were created using a drop-test rig described herein and characterized in three ways: a measure of the coefficient of restitution during impact, investigation of the impact site using an optical interferometer, and fixed ion beam cross sections of select impacts for observation of subsurface damage within the coating and substrate. It was found that hard coatings on softer substrates such as 440C steel were able to mitigate surface damage up to a certain impact speed, depending on the coating, but were unable to influence the coefficient of restitution. On harder substrates like 52100 alloy steel, the coatings were found to increase the coefficient of restitution, indicating a reduction in energy loss due to plastic deformation, and to reduce damage at each tested speed. These effects and their potential influence on bearing performance are discussed in regard to impact mechanics, surface metrology, and the material properties of the coating and substrate acquired by nanoindentation.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.