Abstract
The effect of ultrasonic treatment (UST) on the formation of Fe-rich intermetallics (including sludge) in the A383 alloy is investigated for different processing temperatures in the present study. Differential scanning calorimetry is used to analyze the precipitation temperature of the sludge phase. The results revealed that the sludge will precipitate at a temperature above that of the Al matrix and the precipitation temperature decreases with an increasing cooling rate. UST cavitation applied at different temperatures (600 °C to 750 °C) during the solidification process breaks the sludge into small island-like pieces. However, the aggregation trend of the sludge is not changed. Sludge with small size and uniform distribution is obtained when UST is applied at 600 °C, which is lower than the precipitation temperature of the sludge. At the highest temperature (850 °C), the application of UST has no effect on the formation of either sludge or α-Fe intermetallics. At 750 °C, UST promotes the formation of the sludge when applied at 750 °C.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.