Abstract

The magnetostatic properties of the as-deposited and annealed at T=300 and 400<TEX>$^{\circ}C$</TEX> Ni films were investigated employing both magneto-optical magnetometer and VSM. The Ni films of 50∼200 nm thicknesses were prepared by DC magnetron sputtering technique. The strong influence of annealing temperature on magnetostatic properties of the studied samples was discovered. For the annealed Ni films, the increase of the coercivity H<TEX>$_c$</TEX> (up to 4 times) in comparison with that of as-deposited samples was revealed. The obtained results were explained by using crystallographic structural data of the samples.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.