Amorphous thin films were deposited by radio‐frequency magnetron sputtering at the substrate temperatures of 100, 200, and 300°C, respectively. The electrical properties of thin films were investigated as a function of substrate temperature and film thickness. The leakage current of the films was in the order of to for an applied field of 1 MV/cm. The charge storage capacitances were 7.7 (100°C), 7.9 (200°C), and . Most of the electrical analyses were performed with the data obtained for the thin films deposited at 200°C substrate temperature because they showed optimum electrical properties. The dominant conduction mechanism changed from Schottky emission current at low field to Poole‐Frenkel current at the high field. With increasing film thickness, the surface roughness increased, whereas the transition fields from the electrode‐limited current to the bulk‐limited current process decreased. To verify the effect of this surface roughness on the electrical conduction mechanism, a two‐dimensional numerical simulator, MEDICI, was used to simulate the electric field distribution at the bulk region of the thin film and the interface region between the thin film and electrode. © 1999 The Electrochemical Society. All rights reserved.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.