Abstract
This paper discusses the interaction between superabsorbent polymer (SAP) and alkali-activated slag pastes and the influence of SAP on the properties of the pastes. SAP showed higher absorption in pore solutions extracted from alkali-activated slag pastes compared to that extracted from portland cement paste. Hydrogel desorption in alkali-activated slag matrix activated with Na2CO3 was noticeably delayed compared to alkali-activated slag matrix activated with NaOH matrix or portland cement matrix; this is attributed to a significant delay in the solid skeleton development in this matrix. Addition of SAP was shown to be effective in reducing autogenous shrinkage in alkali-activated slag pastes. A general reduction in compressive strength and electrical resistivity was observed in alkali-activated slag pastes when SAP was added; macrovoid formation and increased overall water/binder are possible reasons for this reduction, respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.