Abstract
This study reports the synthesis of bismuth ferrite ceramics (BiFeO3, BFO) by the sol-gel method and the effect of different sintering temperatures (800 °C, 820 °C, 850 °C, 880 °C, 900 °C) on the crystal structure, morphology, dielectric properties and ferroelectric properties of the bismuth ferrite ceramics. It is observed that the bismuth ferrite phase are formed when the molar ratio of bismuth and ferric is 1.025 : 1, and the bismuth ferrite ceramics have less impurity phase at all the five sintering temperature. The morphology studies revealed that the grain of bismuth ferrite ceramics is spherical and the grain size increases with the increasing of the sintering temperature. When the bismuth ferrite ceramics with excessive bismuth sintered at 820 °C, it exhibits the higher dielectric constant and the lower dielectric loss, the remnant polarization and the coercive field are 0.35 μC/cm2 and 4.03kV/cm, respectively. The observed ferroelectricity in bismuth ferrite ceramics owes to the point defects associated with oxygen vacancy defects as well as the smaller size effect.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.