Abstract
Using ultra-fine alumina powders as raw materials, the submicron transparent alumina with relative density more than 99.9% was fabricated by gelcasting and then sintering-HIP process. It was found that only the samples with relative density more than 95% after presintering could obtain fully densification by post-HIP treatment. The final grain sizes increased after post-HIP treatment and were decided by either HIPing temperature or presintering temperature, depending on which one is higher. The maximal strength can reach about 650MPa when grain size is about 1 μm.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.