Abstract
Ni-YSZ cermets are the most widespread material used as SOFC anodes. These materials are generally fabricated through the reduction of a NiO-YSZ composite, but the reduction conditions have a great effect in the final microstructure of the electrode. In the present work several conditions were explored to reduce microtubular anode supports produced via extrusion in order to find a suitable microstructure for SOFC anodes. Samples were reduced in pure and diluted H2, either dry or humidified at temperatures ranging from 400 to 800°C while their DC conductivity was being monitored. The highest value of peak conductivity was measured in the sample reduced in humidified pure hydrogen at 800°C, but it experienced more severe conductivity degradation that other samples. The best value for the duration of the test was obtained for the sample reduced in dry diluted hydrogen at 800°C.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.