Abstract
Dislocation locking by nitrogen impurities has been investigated in float-zone silicon with nitrogen concentrations of 2.2 x 1015cm-3 and 3 x 1014cm-3. The stress required to unlock dislocations pinned by nitrogen impurities was measured as a function of annealing time (0 to 2500 hours) and temperature (550 to 830°C). For all conditions investigated the locking effect was found to increase linearly with annealing time before saturating. It is assumed that the rate of increase of unlocking stress with annealing time is a measure of transport of nitrogen to the dislocation core. This rate of increase was found to depend linearly on nitrogen concentration, which is consistent with transport by a dimeric species, whose activation energy for diffusion is approximately 1.4eV. The saturation unlocking stress has been found to be dependent on the nitrogen concentration. Additionally, the temperature dependence of the stress required to move dislocations immobilised by nitrogen impurities has been studied. By assuming a value for the binding energy of the nitrogen to the dislocation, the density of the locking species at the dislocation core has been calculated.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.