Abstract
This paper presents the manufacturing process and the results of measurements for aluminum – aluminum oxide materials with addition of glassy carbon particles (GC). The composites were manufactured via high energy milling process with hot pressing subsequently. The influence of mass fraction (5, 10 and 15 wt.%) and a size of GC particles (<40, 40-80, 80-120, 120-160, 160-200µm) on the microstructure and properties were analysed. The complex meaning of GC particles for all, milling process, microstructure and final properties were discovered. After based description of materials, the tribological measurement were performed under two loads – 35 and 50N. It was noted, that mass fraction of GC particles have influence on tribological properties of materials. The composite with 5 wt.% revealed the best friction properties without any significant differences between analysed loads. The influence of particles size proved that the most effective fraction for tribological application is 120 – 160µm.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.