Abstract
Calculated phase diagrams for the Mg–Al–Zn–Mn system indicate that β-Mn(Al) and Al 8Mn 5 can primarily crystallize during the solidification of Mn-modified AZ31. Both phases may act as potential heterogeneous nucleants for Mg grains and thus as potential grain refiners in the Mg–Al system. In this investigation three Mg–3Al–1Zn alloys with different Mn content were die cast and hot rolled at 450 °C. The influence of the Mn content on the microstructural evolution and mechanical properties after hot rolling was studied. After casting, β-Mn and Al 8Mn 5 are present in all three AZ31 alloys without showing a significant influence on the grain size. The potential of β-Mn and Al 8Mn 5 precipitates for grain refinement in AZ alloys is discussed in detail on the basis of solidification kinetics.