The Influence of Magnetic and Dielectric Loss on the Noise Absorption of Iron Particles-Rubber Composites Attached to a Microstrip Line

Abstract

Magnetic and dielectric loss are systematically controlled by using iron flake powders with various initial sizes (7 μm and 70 μm) as the absorbent fillers in the rubber matrix, and their noise absorbing characteristics have been investigated as a function of frequency and sheet thickness. Flake iron particles were prepared by the mechanical forging of spherical powders using an attrition mill. Composite sheets (thickness=0.2 mm-1.0 mm) were prepared with a mixture of iron particles and silicone rubber. Attaching the composite sheets to a microstrip line of 50 Ω, a network analyzer was used to measure the reflection and transmission parameters (S11 and S21, respectively). A nearly constant value of S11 (about −10 dB) was observed, irrespective of particle size. However, S21 is strongly dependent upon initial particle size. For the composites of 7 μm particles (with high magnetic loss), S21 is reduced below −20 dB in the frequency range of 1 GHz to 10 GHz, and the corresponding bandwidth of noise absorption is not so greatly diminished by reducing the sheet thickness as low as 0.2 mm. For the composites of 70 μm particles (with high dielectric loss), however, the bandwidth is greatly reduced with a decrease in sheet thickness. It is concluded that the attenuation of conduction noise through the microstrip line is primarily controlled by the magnetic loss of the iron particles due to strong magnetic field around the microstrip line.