Abstract
In this paper, disruption of brazing process impact on behavior of filler metal and properties of the joint was investigated. Hastelloy X sheet samples were brazed using Ni-13Cr-4Fe-4Si-2,7B filler alloy. Two identical sets of samples were heated in high vacuum, once load reached specified temperature process was interrupted. Subsequently, one set of samples was tested and second set was subjected to rebrazing in proper time and temperature, dedicated for used filler material. Disruption of the process in following temperature was analyzed: 930, 960, 1050, 1127, 1145, 1170°C. After both processes macroscopic observations of joint, peel test, static tensile test and spreadability analysis were carried out.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Scientific Letters of Rzeszow University of Technology - Mechanics
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.