Abstract

The electrochemical behavior and susceptibility to pitting corrosion of CrFeCoNi and CrMnFeCoNi high entropy alloys were studied in a 0.1 M NaCl solution at temperatures ranging from 25 to 75 °C. Electrochemical measurements revealed that CrMnFeCoNi is more susceptible to oxide film breakdown and localized corrosion compared to CrFeCoNi. Post corrosion microscopic observations showed severe pitting corrosion for CrMnFeCoNi in higher temperatures compared to CrFeCoNi. Based on in-depth XPS profile measurements on the remaining oxide films, this behavior was attributed to the depletion of Cr in the oxide film and detrimental presence of Mn in the matrix solid solution of CrMnFeCoNi.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.