Abstract
A method of the reaction hot pressing was used to produce composites from the B4C–(5–15%)(TiH2–VC) system, established the peculiarities of their structures and measured physico-mechanical parameters. The dense dispersion-hardened materials having a high bending strength (Rbm = 420–580 MPa) and increased fracture toughness (KIc = 4.1–4.8 MPa·m1/2) on retention of the HKN = 19–20 GPa are promising for the use in the conditions of the severe abrasive wear.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.