Abstract

This paper presents the results of thermal and microstructural analysis of Cu-Al-Ni shape memory alloy before and after heat treatment. After casting, a bar of Cu-12.8 Al-4.1 Ni (wt.%) alloy, obtained by the vertical continuous casting technique, was subjected to a certain heat treatment procedure. Solution annealing was performed at 850 °C for 60 min, followed by water quenching. Tempering was then performed at four different temperatures (150 °C, 200 °C, 250 °C and 300 °C). The microstructural results were obtained by optical and scanning electron microscopy. Thermodynamic calculation of ternary Cu-Al-Ni system under equilibrium was performed using Thermo-Calc 5 software. Phase transformation temperatures were determined by differential scanning calorimetry (DSC). The DSC results show the highest values of transformation temperatures in as-cast state. After solution annealing and tempering, the transformation temperatures show lower values with exceptional stability of Ms temperature (martensite start temperature).

Full Text
Paper version not known

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call