Abstract
Nitrogen doped 4H-SiC epitaxial layers grown by hot-wall chemical vapor deposition were investigated by deep level transient spectroscopy after irradiation with 6 MeV electrons or 1.6 MeV protons. The influence of silane and propane flows used during the epilayers growth on the behaviour of radiation induced EH6,7 levels is studied. Samples grown under different conditions were investigated: 1 sample grown in steps of different C/Si ratio obtained by changing the propane flow only; 1 sample grown in steps of different C/Si ratio obtained by changing the silane flow only; 2 samples grown with a C/Si ratio of 1.5 but with different flows of propane and silane. These investigations revealed that the low thermal stability of EH6,7 (the defects anneal out at temperatures as low as 750K) is due to the magnitude of silane flow used during the growth irrespective of the C/Si ratio. A possible structure of the EH6,7 defect is discussed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.