Abstract
We have investigated the effect of addition of Gd in Bi 1.8Pb 0.35Sr 1.9Ca 2.1Cu 3Gd x O y superconductor with x=0, 0.1, 0.2, 0.3, 0.4 and 0.5. The samples were prepared by standard solid-state reaction methods. The investigation consisted of X-ray diffraction (XRD), scanning electron microscopy (SEM), dc electrical resistivity, hole concentration and transport critical current density measurements. Transport measurements indicated that the superconducting transition temperature, transport critical current density and hole concentration values of the samples strongly depend on the Gd addition. The values of T c, and J c of the samples decreased with the increase in Gd addition. When Gd addition ratio was increased, surface morphology and grain connectivity of the samples were observed to degrade from SEM investigations and phase ratio of the high- T c (Bi-2223) phase to the low- T c (Bi-2212) phase decreased (XRD measurements). The possible reasons for the observed degradation in superconducting and microstructure properties of Bi-2223 due to Gd addition were discussed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.