Abstract
In this work, discharge operation at a large current density was conducted for strontium-doped lanthanum manganite (LSM) cathodes, and the change in performance and microstructure of the interface between LSM cathode and YSZ electrolyte was investigated. For (La0.8Sr0.2)0.97MnO3 (LSM97) with A-site deficiency, the performance was improved in the initial stage of discharge and then started to deteriorate continuously. The microstructural change in the interface between LSM97 and YSZ was quantitatively analyzed by using a dual-beam focused ion beam-scanning electron microscope. It was found that after discharge at 1.2Acm−2 for 60h, the surface of YSZ electrolyte was covered by a dense layer of LSM, accompanied with the formation of closed nanopores in the internal interface between LSM97 and YSZ. For (La0.8Sr0.2)1.03MnO3 (LSM103) with a slight A-site excess, neither apparent formation of dense LSM103 layer along the LSM103/YSZ interface nor performance deterioration was observed during discharge. The mechanism for the structural change of LSM97 cathode was discussed based on the obtained results.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.