Abstract
ABSTRACT Citric acid can be used as a bio-based binding agent in composites made from lignocellulosic material due to its crosslinking ability with hydroxyl groups via ester formation. Even though plenty of research has investigated diverse manufacturing conditions, with a focus on citric acid content and pressing temperature, an apparent knowledge gap persists regarding their effect on the properties of particleboards made from softwood sawdust. Furthermore, the optimal temperature for particleboards crafted from mostly non-wood lignocellulosic materials was found to be 180–200°C which is lower than that observed for softwood material in a prior study. This study aimed to systematically examine the effects of citric acid content and pressing temperature on particleboards derived from softwood sawdust. Results highlighted a positive correlation of both citric acid content and pressing temperature with mechanical and hygroscopic properties of the particleboards, the best results being achieved at 20 wt% citric acid and 220°C, exhibiting a thickness swelling of 9%, internal bonding strength of 0.77 MPa and a modulus of rupture of 4.3 MPa. This study served as a foundational framework for future investigations into the addition of other chemicals, offering a comprehensive understanding of their interactions with citric acid in particleboard manufacturing.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.