Abstract
Silicate strontium phosphor for white light LEDs was synthesized by high temperature solid-state method. The structure, surface, excitation and emission spectra of Sr3SiO5: Eu2+ phosphor which contain different mass fractions of BaF2 were measured. The results show that BaF2 quantity affects the structure, surface and spectra of Sr3SiO5: Eu2+ sample. The sample has the best properties when the BaF2 concentration comes to 2.0wt%. The structure of sample is tetragonal phase Sr3SiO5. The emission and excitation spectra peaks locate respectively at 575nm and 537nm. The samples can be excited by InGaN blue chip. The emission peaks appeared apparent red shift with the increase of BaF2 concentration. A white light emission spectrum with good color rendition was obtained by coupling the phosphor with blue chip.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.