Abstract
Besides low-temperature molecular beam epitaxy, ion implantation provides an alternative route to incorporate Mn into GaAs above the equilibrium solubility limit. Recently, Mn implanted GaAs diluted magnetic semiconductor was obtained by pulsed laser annealing. However, post-implantation annealing can lead to the formation of secondary phases. In order to compare the post-annealing effect, we investigate GaMnAs by implanting up to 6at% Mn followed by rapid thermal and flashlamp annealing. The structural properties were probed by high resolution X-ray diffraction. The magnetic properties were determined by SQUID measurements. Auger electron spectroscopy has been used to profile the depth distribution of Mn in GaAs after implantation and annealing. We elucidate after implantation a loss of As and that during rapid thermal annealing most of the Mn diffuses towards the surface. Flash lamp annealing prevents out-diffusion, but the recrystallisation efficiency is low. Only the flash lamp annealed samples reveal weak ferromagnetism.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.