Abstract
For the thick steel plate 13MnNiMoNbR, submerged arc welding was carried out, three kinds of wires were used H08Mn2MoA, H10Mn2MoA, H10Mn2Ni2MoA and together with two kinds of fluxes which are SJ101, SJ102 .After welding ,normalizing plus tempering heat treatment was added.Using V-shaped notch Charpy impact test and the fracture morphology was observed for researching. The toughness of weld and heat affected zone was lower than 27J at -20 °C,cleavage fracture exited in main proportion. Experiments proved that because of the slow colling speed of weld after normalizing a large amount of the upper bainite produced. When normalizing temperature fell in the critical zone where the ferrite and austenite two-phase can exist together (critical normalizing),upper bainite in weld was eliminated , strength and low temperature (-20 °C) toughness correspond with national standard.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.