Abstract
The structural and superconducting properties of Bi 1.7Pb 0.3Sr 2Ca 2− x Y x Cu 3O y superconducting samples are investigated by X-ray diffraction (XRD), resistivity and thermoelectric power (TEP) measurements. XRD results reveal that the volume percentage of the 2223 high T c phase decreases with an increase in Y content. The replacement of the Ca 2+ ion by the Y 3+ ion does not influence the tetragonal structure of the pure Bi (Pb): 2223 system and the lattice parameters vary with Y content. The results of resistivity indicate that the critical temperatures T c of the samples decrease monotonically with an increase in Y content. Further, the critical concentration of Y to completely suppress superconductivity in the Y-doped Bi (Pb):2223 system is higher (0.60) than that reported (0.20) for the other rare-earth elements. On the other hand, the values of TEP at room temperature are found to be negative for Y=0.00 and 0.10 samples, and it changed to positive with further increase in Y content. The hole-carrier concentration per Cu ion (P) is deduced by using two different ways: the first in terms of T c values in the superconducting state and the other in terms of TEP values in the normal state. Interestingly, it is found that the values of P deduced from the formal way are not consistent with the reported parabolic behavior for superconducting systems in the under-doped region, and consequently disagree with the general roles of substitution. However, the vice versa is recorded for the values of P deduced from the latter way. The results are discussed in terms of the possible reasons for the suppression of superconductivity in the considered system.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have