The Impact of Pressure Fluctuations on the Early Onset of Stage II Growth of High pH Stress Corrosion Crack

Abstract

Abstract Steel pipelines undergo the following sequential stages prior to high pH stress corrosion cracking (HpHSCC) failure, viz., formation of environmental condition, initiation of the intergranular cracks followed by cracks coalescence to form critical crack size (Stage I), mechanically dictated crack growth with higher rate (Stage II) compared to Stage I, rapid crack propagation to failure (Stage III). From fracture mechanics perspective, the crack size reaches the critical value at the onset of stage II; consequently, stress intensity factor (K) ahead of the crack tip exceed the critical value (KISCC). Although many researches have been devoted to understanding HpHSCC behavior, the mechanical conditions that accelerate the onset of stage II remains unknown. This study investigates the mechanical loading conditions that yield to early onset of stage II with respect to the most severe loading condition in operating pipeline, underload-minor-cycle type of pressure fluctuation. In this study, several loading scenarios were applied to pre-cracked CT specimens exposed to 1 N NaHCO3-1N Na2CO3 at 40° C and −590 mVSCE. The first series of tests were conducted through applying variable amplitude loading waveforms to determine the K value below the KISCC. It was observed the crack growth rate decreases from 1.5 × 10−7 mm/s to 2.5 × 10−8 mm/s when Kmax decreases from 36 to 15 MPa·m0.5. Then, both constant amplitude and variable amplitude loading scenarios with the Kmax = 15 MPa·m0.5 were applied to pre-cracked CT specimens. It was observed that low R-ratio constant amplitude cycles yield to highest crack growth rate (3.6 × 10−7 mm/s), which was one order of magnitude higher than other waveforms. However, comparing the intergranular crack advancement per block resulted in similar crack growth rates for those waveforms containing low R-ratio cycles. These results imply that stage I of crack growth is assisted by fatigue due to low R-ratio cycles. It was observed that loading/unloading frequency of low R-ratio cycles has a direct relation with crack growth rate at stage I, i.e., high frequency cycles accelerate onset of stage II. The implication of these results for pipeline operator is that pressure fluctuation, particularly large and rapid pressure fluctuation at the sites susceptible to HpHSCC, threatens the pipeline integrity. Avoiding such pressure fluctuations, if possible, increase pipeline lifespan and prevents catastrophic damages by intergranular stress corrosion crack growth through delaying the onset of stage II of HpHSCC crack growth.