Abstract
This study used experimental methods to investigate the impact of nitrogen-doped reduced graphene oxide particles (ND-RGOP) reinforcement on thermal and mechanical properties of unidirectional carbon fiber/ epoxy composites (CFRP). In the results, storage modulus and loss modulus significantly increase with the ND-RGOP addition. Besides, glass transition temperature is enhanced with the addition of 0.4 wt% ND-RGOP. In tensile mode, when compared to the baseline (0 weight% ND-RGOP) composites, the elastic modulus in the 0° direction (E1) enhanced by 8.25 % and 11.39 % with 0.4 (0.4 weight%) and 0.8 (0.8 weight%) ND-RGOP addition, respectively. Besides, the ultimate tensile strength of the 0.4 ND-RGOP/CFRP composites significantly reduced by 16.33 % and 53.08 % in both 0° and 90° directions, respectively, as a result of the fracture mechanism changing from fiber pull out and fiber cracking to fiber breakage which was confirmed by SEM investigations. Furthermore, both the compressive modulus and the shear modulus increased with ND-RGOP reinforcement over 10 %, although the ultimate compressive strength decreases with low ND-RGOP reinforcement. In conclusion, low concentrations of ND-RGOP addition improves the thermal and mechanical properties of CFRP laminates in elastic region, although high concentrations of ND-RGOP decreases the thermal properties.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.