Abstract
To better understand the relations between deposition conditions, microstructure, H incorporation and the optoelectronics properties of undoped a-Si1−x Gex:H alloys, we performed a comparative study of samples (with x≈0.5) prepared by plasma enhanced chemical vapour deposition at total pressures varying from 900 to 2200 mTorr. The hydrogen bonding, detected by infra-red absorption measurements and H thermal desorption experiments, as well as the optoelectronic properties, determined by a combination of standard optical and photothermal deflection spectroscopy measurements, were found to depend on the total pressure. The results obtained in the as-deposited state and after annealing at increasing temperatures are analysed as a whole in terms of specific local H bonding environment, degree of order, and defects.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.