Abstract
The hydration characteristics and expansion impetus of three kinds of cement paste under free-and confined-curing conditions were investigated, which were respectively mixed with three different kinds of expansive agent at low W/B ratio. The results show that the hydration products of pure cement paste and paste mixed with expansive agent are same, but the amount of hydration products, un-hydrated C3S and C2S are obviously different at the same hydration age. At 3 d age, the amount of CH in pure cement paste is less than that of paste mixed with expansive agent, but it is reverse when at 28 d age. The amount of AFt at 3d and 28d age in pure cement paste is less than those of paste mixed with expansive agent. Regardless of under free- or confined-curing condition, the amount of ettringite produced varies little since 3d age. The joint effect of the tumefaction of gel-ettringite due to water absorption and the expansive pressure on the pore caused by the crystalloid ettringite is the cause of the volume expansion of cement paste, and the former effect is much greater than the latter.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Wuhan University of Technology-Mater. Sci. Ed.
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.