Abstract
This study was aimed at experimentally investigate the formation of zeolite-A and zeolite-X through geopolymerization routes. The samples were prepared by alkali-activation of metakaolinite at 70 °C with Si:Al = 1.04 and 1.25 and Na:A l= 0.6, 0.8, 1.0 while keeping the molar ratio of H2O:Na2O = 10. The physical and mechanical properties of the resulting materials were characterized by means of bulk density and porosity measurement, compressive strength and Vickers microhardness tests. Crystallinity level and the phase of the samples was examined by X-Ray Diffraction (XRD) while morphology and elemental composition of the samples were examined by Scanning Electron Microscopy (SEM) and Energy Dispersive Spectroscopy (EDS). It was found that zeolite-A and zeolite-X were able to produce through geopolymerisation of metakaolin. XRD and SEM-EDX analysis results showed that these materials were composed of zeolite-A or zeolite-X together with amorphous geopolymer. The zeolite X was only formed when ratio of Si:Al is 1.25 while zeolite A was formed at all ratio except ata Si:Al=1.25 and Na:Al=1.0. These materials have relatively low hardness and compressive strength, low density and high apparent porosity.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.