Abstract
The microstructures and shear strength of the interface between Sn–Zn lead-free solders and Au/Ni/Cu interface under thermal aging conditions was investigated. The intermetallic compounds (IMCs) at the interface between Sn–Zn solders and Au/Ni/Cu interface were analyzed by field emission scanning electron microscopy and transmission electron microscopy. The results showed the decrease in the shear strength of the interface with aging time and temperature. The solder ball with highly activated flux had about 8.2% increased shear strength than that with BGA/CSP flux. Imperfect wetting and many voids were observed in the fracture surface of the latter flux. The decreased shear strength was influenced by IMC growth and Zn grain coarsening. In the solder layer, Zn reacted with Au and then was transformed to the β-AuZn compound. Although AuZn grew first, three diffusion layers of γ-Ni 5Zn 21 compounds were formed after aging for 600 h at 150 °C. The layers divided by Ni 5Zn 21 (1), (2), and (3) were formed with the thickness of ∼0.7 μm, ∼4 μm, and ∼2 μm, respectively.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.