Abstract
Nowadays, the utilization of oil palm trunk (OPT) biomass has gained more interest in composite applications. This research presents the flexural properties of unimpregnated OPT and OPT impregnated with epoxy (OPTE) composites. The OPTE composites were fabricated using the vacuum-assisted resin transfer moulding (VARTM) technique. The unimpregnated OPT and OPTE composite specimens were selected from three different zones of longitudinal zone OPT namely Zone I (outer), Zone II (middle) and Zone III (inner), respectively. The flexural test was conducted according to ASTM D790. The results showed promising increases in flexural strength and flexural modulus of the OPTE composite in Zones I, II, and III compared to unimpregnated specimens, with increases of 254.09 % (49.79 MPa) and 158.78 % (4.14 GPa) in Zone I, 297.43 % (37.28 MPa) and 309.51 % (3.58 GPa) in Zone II, and 242.67 % (29.34 MPa) and 305.84 % (2.94 GPa) in Zone III, respectively. There was positive trend linear regression significantly observed in the relationship between flexural strength and modulus of elasticity (MOE) of OPTE composites and unimpregnated OPT of all three zones, respectively. The fractured flexural specimens of three different zones were analysed by using scanning electron microscopy (SEM). The improvement of OPTE composites is a possible as an alternative to replace the existence of commercial wood.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.