Abstract
In this research, the flame retardancy of neat alginate fiber, flame retardant viscose fiber (FRV) and alginate/FRV (50/50) blending fibers were investigated by vertical burning and cone calorimeter tests. The vertical burning test showed that the afterflame time of alginate fiber was 0s, but alginate presented serious smoldering behavior with the afterglow time of 605s and damaged length of 85mm, while the afterglow time of FRV was 0s. When the FRV was incorporated into alginate with the weight ratio of 50/50, the afterglow time and damaged length were significantly reduced to 85s and 35mm, indicating the smoldering of alginate can be effectively decreased. The morphology and chemical structure of the alginate residual demonstrated that it was seriously destroyed during smoldering process, which was ascribed to its relative low initial thermal degradation temperature. Based on the thermal properties analysis, alginate and FRV fibers shared the concurrence of rapid degradation in the same temperature region of 250–300°C, through which, the compact and stable char formed by FRV can prevent the heat transmission and suppress the smoldering of alginate. Further, the cone calorimeter results demonstrated that the time to ignition (TTI) significantly increased and peak heat release rate (PHRR) decreased for alginate/FRV (50/50) compared with FRV. With this research, a new method to overcome the smoldering of alginate was proposed by blending with FRV
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.