Abstract
Abstract Fatigue specimens of A508-3 steel were irradiated in the swimming-pool test reactor in China Institute of Atomic Energy, the fluence was 3 × 10 19 n/cm 2 at 300 °C, then low-cycle fatigue tests were carried out at ambient temperature, with the fatigue strain range is 0.32–1.8%. The results indicate that, irradiated A508-3 specimens exhibit cyclic softening and instability behavior during the test, and the cyclic softening rate increased with strain range increased; fatigue life decreased from 1.7 × 10 5 to about 5 × 10 2 , as the strain range increased from 0.32% to 1.8%, the fatigue life of A508-3 steel increased after the neutron irradiation; fatigue fracture initiated at the surface of specimen, and more individual cracks formed on the specimens of higher strain range compared with the specimens of lower strain range.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.