Abstract
The failure of drill pipe occurs frequently in oil and gas wells and seriously affects the safety and efficiency of drilling operations. Therefore, this paper clarifies the main failure patterns and reasons of drill pipes, and puts forward the analysis process and method of pipe failures. The case of failure S135 drill pipe was investigated through a series of experimental tests and mechanical simulation. The results showed that the physical and chemical performance of pipe material met the requirements of API Spec 5DP-2020, and the fracture of pipe body belonged to overload ductile fracture. The drill pipe Ni-plating was damaged and the exposed matrix was corroded and scoured. The crack originated from the corrosion pit on the inner wall because of stress concentration, and extended along the circumference during the operation of lifting drill pipe for many times, and finally led to fracturing suddenly. In addition, some suggestions are given to prevent similar failures.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.