Abstract
The reliability of Sn-3.0Ag-0.5Cu (SAC 305) solder joint under a broad level of drop impacts was studied. The failure performance of solder joint, failure probability and failure position were analyzed under two shock test conditions, i.e., 1000 g for 1 ms and 300 g for 2 ms. The stress distribution on the solder joint was calculated by ABAQUS. The results revealed that the dominant reason was the tension due to the difference in stiffness between the print circuit board and ball grid array, and the maximum tension of 121.1 MPa and 31.1 MPa, respectively, under both 1000 g or 300 g drop impact, was focused on the corner of the solder joint which was located in the outmost corner of the solder ball row. The failure modes were summarized into the following four modes: initiation and propagation through the (1) intermetallic compound layer, (2) Ni layer, (3) Cu pad, or (4) Sn-matrix. The outmost corner of the solder ball row had a high failure probability under both 1000 g and 300 g drop impact. The number of failures of solder ball under the 300 g drop impact was higher than that under the 1000 g drop impact. The characteristic drop values for failure were 41 and 15,199, respectively, following the statistics.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.